Morphological and optical properties of PdxAg1-x alloy nanoparticles

Alloy nanoparticles (NPs) can offer a wide range of opportunities for various applications due to their composition and structure dependent properties such as multifunctionality, electronic heterogeneity, site-specific response, and multiple plasmon resonance bands. In this work, the fabrication of self-assembled Pd_xAg_1-x NPs alloy nanostructures with distinct size, density, shape, and composition is demonstrated via the solid-state dewetting of sputtered Pd/Ag thin films on c-plane sapphire. The initial stage of bilayer dewetting exhibits the nucleation of voids, followed by the expansion of voids and cluster breakdown and finally shape transformation along with the temperature control. Bilayer composition shows a substantial influence on the dewetting such that the overall dewetting is enhanced along with the increased Ag composition, i.e. Pd_0.25Ag_0.75 > Pd_0.5Ag_0.5 > Pd_0.75Ag_0.25. On the other hand, the size and density of NPs can be efficiently controlled by varying the initial thickness of bilayers. Reflectance peaks in UV and near-infrared (NIR) regions and a wide absorption band in the visible region arisen from the surface plasmon resonance are observed in reflectance spectra. The peak intensity depends on the composition of Pd_xAg_1-x NPs and the NIR peaks gradually blue-shift with the size decrement.     

基于连续介质损伤力学的7075铝合金高温成形极限理论预测与数值仿真

开展7075铝合金高温单向拉伸试验和成形极限试验，获得了不同温度和应变率的应力-应变曲线和成形极限曲线。结果表明，在较高的温度和应变率时7075铝合金的强度减小、成形性提高。为描述7075铝合金高温损伤演化过程，提出一种改进的连续介质损伤模型，并建立了耦合损伤的多轴统一黏塑性本构模型。基于试验结果，运用NSGAII遗传算法标定了模型中的参数，标定后的本构模型可以很好地预测7075铝合金的高温热力行为和极限应变。通过有限元软件Abaqus的用户材料子程序VUMAT，该本构模型被编入到Abaqus软件中进行数值仿真计算。结果表明，仿真获得的成形极限曲线和应变场分布与试验和理论结果吻合度好，进一步证明了所建立的耦合损伤的多轴本构模型的正确性及其在高温成形极限有限元仿真中的适用性。     

Microstructure and mechanical properties of Mg-5Li-1Al sheets prepared by accumulative roll bonding

Ultrafine-grain and high-strength Mg-5Li-1Al sheets were prepared by accumulative roll bonding (ARB) process. Evolution of microstructure and mechanical properties of ARB-processed Mg-5Li-1Al sheets was investigated.Results show that, during ARB process, the evolution of deformation mechanism of t Mg-5Li-1Al alloy is as follows: twinning deformation, shear deformation, forming macro shear zone, and finally dynamic recrystallization (DRX). The grain refining mechanism changes from twin DRX to rotation DRX. With the increase in ARB cycles, strength of the Mg-5Li-1Al sheets is enhanced, whilst elongation varies slightly. With the increase in rolling cycles, anisotropy of mechanical properties decreases. It is conclusive that strain hardening and grain refinement dominate the strengthening mechanism of Mg-5Li-1Al alloy.     

Ti70合金板的组织与力学性能的各向异性

通过拉伸及低温冲击试验、光学显微镜、扫描电镜及X射线衍射仪,对Ti70合金板的组织与力学性能的各向异性进行了研究。结果表明,Ti70合金板热轧及退火后组织未出现明显差异,退火过程中主要以回复为主,但在高密度位错的剪切带上出现了一定数量的再结晶晶粒。退火态Ti70合金板横向屈服强度及低温冲击吸收能量都高于纵向,但抗拉强度低于纵向,表现出了明显的各向异性。退火后Ti70合金板形成了较强的{0002}基面织构,其晶面法向向RD方向(纵向)偏转±30°,向TD(横向)方向偏转±41°。由于基面织构更向RD方向集中,因此造成了Ti70合金板力学性能的各向异性。     

热处理对等离子喷涂铁基非晶合金涂层微观结构和耐腐蚀性能的影响

采用等离子喷涂技术在Q235钢基体上制备Fe48Cr15Mo14C15B6Y2非晶合金涂层,之后对涂层进行200,300,500,600,700℃热处理,研究了热处理对涂层微观结构、耐电化学腐蚀性能和耐均匀腐蚀性能的影响。结果表明:随着热处理温度的升高,涂层的非晶含量降低,孔隙率先减小后增大,经300℃热处理后涂层的孔隙率最低,且低于未热处理涂层的;热处理后涂层中的晶体相主要包括α-Fe,Fe-Cr,Fe63Mo37,Fe3C等;随着热处理温度的升高,涂层的自腐蚀电流密度先减小后增大,经300℃热处理后,自腐蚀电流密度最小,涂层的耐电化学腐蚀性能最好;经过热处理后,涂层在NaCl溶液中浸泡31d后的单位面积质量损失减小,且热处理温度越高,单位面积质量损失越小,涂层的耐均匀腐蚀性能提高。     

激光立体成形TC4钛合金的热力场演化

激光立体成形能够实现高性能复杂零件的精确成形，但成形过程中的高温度梯度极易导致残余应力和变形，最终影响构件的几何精度和力学性能。通过搭建基板单边夹持原位热变形测量系统，探究了多道多层TC4钛合金成形件在激光立体成形过程中基板温度、变形的演化规律，分析了不同扫描策略对构件热应力场的影响。研究结果表明，构件的变形发展受其热历史驱使，扫描策略对成形件的热变形具有显著影响。     

双态组织高Nb-TiAl合金的缺口敏感性

通过对圆棒状缺口试样和无缺口光滑试样进行单向拉伸试验,研究了双态组织高Nb-TiAl合金的缺口敏感性。研究表明,缺口根半径R≥0. 5 mm的U型试样和缺口角度60°、R≥1 mm的V型试样的抗拉强度RmN都大于光滑试样的抗拉强度Rm,缺口敏感度NSR均大于1,合金对缺口不敏感。当缺口类型相同时,缺口敏感性随缺口根半径R的减小而增大; V型缺口敏感性大于U型缺口;对于V型缺口试样,当R=0. 5 mm时,其NSR在0. 98～1. 03之间,RmN在Rm附近波动,易出现缺口敏感。     

A dense and compact laser cladding layer with solid metallurgical bonding significantly improved corrosion resistance of Mg alloy for engineering applications

Although Mg alloy attracts great attention for engineering applications because of high specific strength and low density, low corrosion resistance limits its extensive use. In this study, Mg–Al–Zn–Mn alloy was treated via a laser cladding process to generate a dense and compact laser cladding layer with solid metallurgical bonding on the substrate for improving corrosion resistance, effectively hindering the corrosion pervasion into Mg alloy. The corrosion current density declined from 103 μA/cm² for Mg alloy to 13 μA/cm² for the laser cladding layer in NaCl aqueous solution. Moreover, the laser cladding layer was slightly corroded in comparison with Mg alloy in NaCl aqueous solution. Besides, the microhardness of the cladding layer reached a mean value of 170.5 HV, 3.1 times of Mg alloy (56.8 HV) due to the in situ formation of hardening intermetallic phases. Wear resistance of laser cladding layer was also obviously improved. These results demonstrated that the laser cladding layer obviously enhanced anticorrosion property of Mg alloy for engineering applications.     

Effects of isothermal treatment parameters on the microstructure of semisolid alloys

Cold-rolled 6061 aluminium alloys are used to prepare semisolid billets by recrystallisation and partial melting. The effects of isothermal treatment parameters on the microstructures were investigated. The results indicated that the high isothermal holding temperature increases the experimental liquid fraction, average grain size and shape factor. A long isothermal holding time also increases the experimental liquid fraction and improves the spheroidisation degree of solid grains, but the average grain size also increases. Moreover, when the isothermal holding time at high temperature is increased, the size of intragranular liquid droplets increases, but their quantity decreases. The optimal isothermal holding temperature and time during semisolid isothermal treatment were 635°C and 5?–?10?min, respectively.     

自保护药芯焊丝明弧堆焊Fe-Cr-C-B-W合金的组织及性能

采用自保护药芯焊丝明弧堆焊技术制备五组不同钨含量的Fe-Cr-C-B-W合金. 借助金相显微镜、扫描电子显微镜、X射线衍射仪、洛氏硬度计和磨损试验机分析堆焊合金的组织及性能. 结果表明，合金的显微组织由马氏体、残余奥氏体、M₇(C,B)₃，M₃(C,B)，Fe₃W₃C和WC组成. 大部分钨元素被迁移到晶界生成了比WC稳定性更好的Fe₃W₃C缺碳复合相，堆焊层中没有典型的初生WC硬质相颗粒生成. 随着钨添加量的增多，共晶硬质相M₇(C,B)₃，M₃(C,B)和Fe₃W₃C随之增多，间距减小，呈连续网状均匀分布. 当钨的添加量为12%时，堆焊层的耐磨性达到最佳.